17-4PH

17-4PH

17.4PH, 0Cr17Ni4Cu4Nb, SAE AMS 5342E (2006) Steel, Corrosion-Resistant, Investment Castings 16Cr - 4 1Ni - 0 28Cb (Nb) - 3 2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4) Used typically for parts requiring good corr

17-4PH数据表下载

17-4PH化学成分 - SAE AMS 5342E (2006)

C Si Mn Cr Ni Cu Nb
≤0.07
≤1.00
≤1.00
15.00-17.50
3.00-5.00
3.00-5.00
0.15-1.45

17-4PH标准规范

  • SAE AMS 5342E (2006) - Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4)
  • SAE AMS 5343E (2006) - Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1000) 150 ksi (1034 MPa) Tensile Strength (17-4)
  • SAE AMS 5344F (2007) - Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H900) 180 ksi (1241 MPa) Tensile Strength (17-4)
  • SAE AMS 5604G (2013) - Steel, Corrosion Resistant, Sheet, Strip, and Plate 16.5Cr - 4.0Ni - 4.0Cu - 0.30Cb Solution Heat Treated, Precipitation Hardenable
  • SAE AMS 5622F (2013) - Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution Heat Treated, Precipitation Hardenable Consumable Electrode Remelted
  • SAE AMS 5643/H1150 (2013) - Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing and Rings 16Cr – 4.0Ni – 0.30Cb (Nb) – 4.0Cu Solution and Precipitation Heat Treated (H1150)
  • SAE AMS 5643S (2013) - Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution Heat Treated, Precipitation Hardenable

  • 17-4PH机械性能

    热处理 最小值 最大值 近似值 备注
    热处理 最小值 最大值 近似值 备注
    热处理 最小值 最大值 近似值 备注
    热处理 最小值 最大值 近似值 备注
    热处理 最小值 最大值 近似值 备注
    热处理 Type 最小值 最大值 近似值 备注

    SAE AMS 5342E (2006) Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4) Used typically for parts requiring good corrosion resistance and strength up to 315°C.


    17-4PH库存信息

    钢号 规格mm 重量kg
    φ70 x 7000mm
    0.73
    φ80 x 7000mm
    1.223
    φ95 x 5500mm
    0.7
    φ95×16x4500mm
    1400
    φ105×10x7000mm
    3700

    17-4PH产品形态